KINETIC CHARACTERIZATION OF GAG:CE PHOSPHOR

Abstract

Thermoluminescence (TL) kinetic characterization of cerium (Ce3+)doped gadolinium aluminum garnet (GAG) prepared bywet chemical synthesis method arepresented in this study. Thermoluminescenceglow curve of GAG phosphor after UV irradiated has two peaks at about 350 and 501K with a heating rate of 2 Ks-1. Thermoluminescence kinetic parameters such asorder of kinetics, frequency factor and activation energy associated with the mainglow peak of the GAG:Ce phosphor have been calculated using various heatingrates (VHR) computerized glow curve deconvulation (CGCD) and peak shape (PS) methods in this study. Theactivation energies obtained by VHR, PS and CGCD methods are calculated to be1.24, 1.11 and 1.14 eV, respectively. The frequency factors attained by these methodswere found as 3.41x1011, 1.80x1010 and 2.63x1010s-1, respectively. Results acquired using all methods are discussed andcompared.

Buçalışmada, ıslak kimyasal sentez metodu ile hazırlanmış seryum (Ce+3)katkılı gadolinyum alüminyum garnetin termolüminesans (TL) kinetikkarakterizasyonu sunulmuştur. UV ile ışınlanmasının ardından GAG fosforunun, termolüminesansışıma eğrisi 2 Ks-1ısıtma hızı ile yaklaşık olarak 350 ve 501 K de iki pike sahiptir. ÇalışmadaGAG:Ce fosforunun ana ışıma piki (501 K) ile ilişkili kinetik derece, frekansfaktörü ve aktivasyon enerjisi gibi termolüminesans kinetik parametreleri,çeşitli ısıtma hızları (VHR), bilgisayarlı ışıma eğrisi dekonvulasyonu (CGCD)ve pik şekli (PS) metotları ile hesaplanmıştır. VHR, PS ve CGCD metotları ile elde edilen aktivasyon enerjileri sırasıyla 1,24,1,11 ve 1, 14 eV olarak hesaplanmıştır. Bu metotlarla ulaşılan frekansfaktörleri 3,41x1011, 1,80x1010 ve 2,63x1010 s-1olarak bulunmuştur. Tüm metotlardan elde edilen sonuçlar kıyaslanmış vetartışılmıştır.